XOANONS?Additive
JIAZHI? Easy-cleaning functional resin
Model number
JIAZHI®JZ-9562-10
Specification
Composition: Silicon modified hydroxyl acrylic resin solution
Appearance: Clear to slight yellowish liquid
Solvent: PMA
Content: 54±3%(140℃ 2h)
Viscosity: 100-1000mPa·s
(Rotating viscometer)(25±0.2)℃
Hydroxyl value: 179±5 mg KOH/g
(Theoretical value of solid resin)
Note: This data sheet is intended to give typical results, not
standard.Subject to COA.
Application system
Solvent-based
Properties
Increase slip. Improve hydrophobicity and oleophobicity.
Provide anti-marker wiping performance.
Provide lotus effect.
Excellent flexibility .
Excellent performance of carburetor cleaning agent.
Excellent hot-healing function.
Water contact angle ＞100°
Excellent weather resistance.
Storage stability
Keep intact 36 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.
Recommended formula
1. Suggestion for PU varnish formulation
|
|
Material |
Dosage% |
|
Part A |
JZ-9562-10 |
76.00 |
|
PMA |
22.75 |
|
|
Dryer(1%) |
1.00 |
|
|
WE-D8920BR(leveling agent) |
0.25 |
|
|
Total |
100 |
|
|
Part B |
N3390 |
29.4 |
Note：
1.NCO% of CORONATE=16.4, produced by TOSOH, Japan.
2.The mixed part A and B should be used up within 5-7 hours in a sealed container. Otherwise, the mixed material will be gelled.
3.Suggest dry it at 110-130℃ for 2-3min. for automotive protective film, ripening at 60-80℃ more than 24h. Dry it at 80℃ for 1h, or 150 ℃ for 5h for other industrial coatings.
Note: the advantages and disadvantages of fouling resistance and aging resistance depend on whether the coating is fully cross-linked; it is an effective method to put the surface treated film into the ripening box. It takes at least 24 hours during ripening, and the effect is better if it can reach more than 48 hours.
Package
25KG / 180KG
Application suggestion for paint protective film
|
item |
TPH film base |
TPU film base |
|
fouling-resistance from dry wiping |
no residue |
no residue |
|
fouling-resistance from alcohol wiping |
no residue |
no residue |
|
hydrophobicity |
water contact angle＞100° |
water contact angle＞100° |
|
flexibility |
elongation＞80% |
elongation＞70% |
|
recovery |
hot healing |
hot healing |
|
chemical resistance |
No change after volatilization drying |
No loss of gloss No loss of gloss |
|
weather resistance |
aging test of QUVB 1000h |
aging test of QUVB 1000h |
Instructions:
1. Baking conditions :110-130℃ 3min
Maturation conditions: 80 ℃ 48h
Coating thickness: TPH base 8-10μm TPU base 15-20μm
In view of the variability of substrate, film thickness, baking and aging conditions, the data provided in this table are for reference only.
2. Oil pen is used for pollution resistance test. The test method is to write on the film and place the film at room temperature for 3 min
3. The brand of carburetor cleaner used in chemical resistance test is Bontny.