Anhui Xoanons Chemical Co.,Ltd.

Anhui Xoanons Chemical Co., Ltd.

PRODUCTS

XOANONS?Additive

Surfactant
Polyacrylate leveling agent
Fluorocarbon modified polyacrylate leveling agent
Fluorine surfactant
Polyether modified silicon leveling agent
Reactive silicon additive with acrylic functional group
Substrate wetting agent
Anti-graffiti additive
Performance enhancer
Dispersant
Defoamer

JIAZHI? Easy-cleaning functional resin

Anti-graffiti and Anti-adhesive Resin for municipal engineering paint
Anti-pollution and rain-resistant resin for protective film of paint
Easy-cleaning resin for industrial paint
Anti-icing resin
Anti-graffiti resin for automotive leather and sofa leather
Anhui Xoanons Chemical Co.,Ltd.

PRODUCTS

JIAZHI?JZ-9562-10

Model number
JIAZHI®JZ-9562-10

Specification
Composition: Silicon modified hydroxyl acrylic resin solution
Appearance: Clear to slight yellowish liquid
Solvent: PMA
Content: 54±3%(140℃ 2h)
Viscosity: 100-1000mPa·s
(Rotating viscometer)(25±0.2)℃
Hydroxyl value: 179±5 mg KOH/g
(Theoretical value of solid resin)
Note: This data sheet is intended to give typical results, not
standard.Subject to COA.

Application system
Solvent-based
Properties
Increase slip. Improve hydrophobicity and oleophobicity.
Provide anti-marker wiping performance.
Provide lotus effect.
Excellent flexibility .
Excellent performance of carburetor cleaning agent.
Excellent hot-healing function.
Water contact angle >100°
Excellent weather resistance.

Storage stability
Keep intact 36 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Recommended formula
1. Suggestion for PU varnish formulation

 

Material

Dosage%

Part A

JZ-9562-10

76.00

PMA

22.75

Dryer(1%)

1.00

WE-D8920BR(leveling agent)

0.25

Total

100

Part B

N3390

29.4

Note:
1.NCO% of CORONATE=16.4, produced by TOSOH, Japan.
2.The mixed part A and B should be used up within 5-7 hours in a sealed container. Otherwise, the mixed material will be gelled.
3.Suggest dry it at 110-130℃ for 2-3min. for automotive protective film, ripening at 60-80℃ more than 24h. Dry it at 80℃ for 1h, or 150 ℃ for 5h for other industrial coatings.
Note: the advantages and disadvantages of fouling resistance and aging resistance depend on whether the coating is fully cross-linked; it is an effective method to put the surface treated film into the ripening box. It takes at least 24 hours during ripening, and the effect is better if it can reach more than 48 hours.

Package
25KG / 180KG

Application suggestion for paint protective film

item

TPH film base

TPU film base

fouling-resistance from dry wiping

no residue

no residue

fouling-resistance from alcohol wiping

no residue

no residue

hydrophobicity

water contact angle>100°

water contact angle>100°

flexibility

elongation>80%

elongation>70%

recovery

hot healing

hot healing

chemical resistance
(Carburetor-resistance cleaner)

No change after volatilization drying

No loss of gloss No loss of gloss

weather resistance

aging test of QUVB 1000h

aging test of QUVB 1000h

Instructions:
1. Baking conditions :110-130℃ 3min
Maturation conditions: 80 ℃ 48h
Coating thickness: TPH base 8-10μm TPU base 15-20μm
In view of the variability of substrate, film thickness, baking and aging conditions, the data provided in this table are for reference only.

2. Oil pen is used for pollution resistance test. The test method is to write on the film and place the film at room temperature for 3 min

3. The brand of carburetor cleaner used in chemical resistance test is Bontny.