Purpose: performance evaluation of XOANONS^?WE-D210
1.Dispersing titanium white in polyester amino resin system
1.1 grinding prepare

Component	Dosage(g)
Saturatedpolyesterresin	30
Dispersingagent	0.7
Titaniumwhite(BLR-699)	35
Mixedsolvent	11.1
Total	76.8

1.2 fineness and viscosity

Storagetime	Dispersingagent	fineness		viscosity
		1h	2h
Beforestorage	Similarproduct	15	15	Thesamewithalowviscosity
	XOANONS?WE-D210	15	15
Storefor10dayat50℃	Minimalchanginginfinenessandviscosity

1.3 Preparation of paint. Distribute the paint over the black&white cardboard. Drying for 1min at 280℃.

Component	Dosage(g)
Whitepaste	76.8
Saturatedpolyesterresin	12
Methylatedaminoresin	8
XOANONS?WE-D887	0.4
Acidcatalyst	0.4
Mixedsolvent	2.4
Total	100

1.4 data sheet before storage

Dispersingagent	opacity	L	20°gloss
Similarproduct	86.83	94.02	62.60
XOANONS?WE-D210	87.40	94.10	63.40

1.5 data sheet after storage 10days at 50℃

Dispersingagent	opacity	L	20°gloss
Similarproduct	86.04	93.74	64.60
XOANONS?WE-D210	87.95	93.91	65.40

2. Dispersing titanium white in thermoplastic acrylic resin system 2.1 grinding prepare

Component	Dosage(g)
Thermoplasticacrylicresin	59.7
Dispersingagent	0.3
Titaniumwhite(BLR-699)	30
Mixedsolvent	10
Total	100

2.2 fineness and viscosity

Storagetime	Dispersingagent	fineness		viscosity
		1h	2h
Beforestorage	Similarproduct	15	15	Thesamewithalowviscosity
	XOANONS?WE-D210	15	15
Storefor10dayat50℃	Minimalchanginginfinenessandviscosity

2.3 Preparation of paint
2.3.1 medium-gloss paint: Dilute paste(5g) with solvent(2g). Distribute the paint over the black&white cardboard.Self-drying.
2.3.2 high-gloss paint: Dilute paste(3g) with solvent(2g) and resin(3g). Distribute the paint over the black&white cardboard.Self-drying.
2.4 data sheet before storage

Item	Dispersingagent	opacity	L	20°gloss	60°gloss
Medium-gloss	Similarproduct	73.50	94.25	——	59.90
	XOANONS?WE-D210	74.45	94.38	——	61.70
High-gloss	Similarproduct	69.03	93.74	61.00	——
	XOANONS?WE-D210	69.89	93.79	63.30	——

2.5 data sheet after storage 10days at 50℃

Item	Dispersingagent	opacity	L	20°gloss	60°gloss
Medium-gloss	Similarproduct	73.29	94.14	——	65.30
	XOANONS?WE-D210	74.32	94.26	——	65.20
High-gloss	Similarproduct	77.85	93.67	65.70	——
	XOANONS?WE-D210	78.04	93.82	66.80	——

3. Dispersing titanium white in hydroxyl acrylic resin system 3.1 Grinding prepare

Component	Dosage(g)
Hydroxylacrylic	33.6
Dispersingagent	0.5
Titaniumwhite(BLR-699)	50
Mixedsolvent	15.9
total	100

3.2 fineness and viscosity

Storagetime	Dispersingagent	fineness		viscosity
		1h	2h
Beforestorage	Similarproduct	15	12.5	Thesamewithalowviscosity
	XOANONS?WE-D210	15	12.5
Storefor10dayat50℃	Minimalchanginginfinenessandviscosity

3.3 Preparation of paint. Paste(4g) + hydroxyl acrylic resin(1g)+ solvent(2g)+ curing agent(1g). Distribute the paint over the black&white cardboard. Drying for 30min at 90℃. 3.4 data sheet before storage

Dispersingagent	opacity	L	20°gloss
Similarproduct	73.91	93.95	80.30
XOANONS?WE-D210	74.06	93.94	81.90

3.5 data sheet after storage 10days at 50℃

Dispersingagent	opacity	L	20°gloss
Similarproduct	76.30	94.28	81.60
XOANONS?WE-D210	77.90	94.38	81.20

4. Dispersing titanium white in alkyd resin 4.1 grinding prepare

Material	Dosage(g)
Alkydresin(dilutedtocontent50%)	33.6
Dispersingagent	0.5
Titaniumwhite(BLR-699)	50
Mixedsolvent	15.9
total	100

4.2 fineness and viscosity

Storagetime	Dispersingagent	fineness		viscosity
		1h	2h
Beforestorage	Similarproduct	15	12.5	Thesamewithalowviscosity
	XOANONS?WE-D210	15	12.5
Storefor10dayat50℃	Minimalchanginginfinenessandviscosity

4.3 preparation of paint Paste(4g)+ alkyd resin(1g)+ solvent(2g)+ curing agent(1g). Distribute the paint over the black&white cardboard. Drying in 30min at 90℃. 4.4 data sheet before storage

Dispersingagent	opacity	L	20°gloss
Similarproduct	74.22	93.62	83.00
XOANONS?WE-D210	75.13	93.68	82.80

4.5 data sheet after storage 10days at 50℃

Dispersingagent	opacity	L	20°gloss
Similarproduct	76.28	94.02	83.40
XOANONS?WE-D210	76.78	93.28	83.60

Note：Opacity indicates the ability of the substrate surface coating cover color. Higher value, better covering power. L means light. Higher value, much whiter of coat film and vice versa.